Synthetic Staple PVA Fiber for Good Substitution of Asbestos

• After-sales Service: None
• Material: Polyvinyl Alcohol
• Diameter (Dtex): 2.0+/-0.25
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Tensile Strength (Cn/Dtex): 11.5 Min.
• Modulus (Cn/Dtex): 280+/-20
• Elongation %: 7.5max.
• Density (g/cm3): 1.29
• Hot Water Decrement: 2%Max.
• Length: 6mm,12mm
• Transport Package: 180kgs Net Per Woven Plastic Bag
• Specification: 100% PVA fiber
• Trademark: Briture
• Origin: China
• Production Capacity: 5000metric Ton/Year
• Package Size: 190.00cm * 180.00cm * 170.00cm
• Package Gross Weight: 200.500kg

Product Description

Product Description

1. It is with the purpose of high modulus, high strength, alkali and acid resistance, heat resistance. It also has good compatibility with cement and other macromolecule material. 

2. It is mainly used in construction and cement industry, such as cement board, non asbestos material for heat and attrition resistance,plastic and rubber reinforcement. 

3. It is the good substitution of Asbestos. 
4. Dosage: fiber:cement=1:50 by weight

 

Specification

Material	Polyvinyl Alcohol
Diameter (dtex)	2.0+/-0.25
Tensile Strength (cN/dtex)	11.5 min.	13min.
Modulus (cN/dtex)	280+/-20	300min.
Elongation %	7.5max.
Density (g/cm3)	1.29
Hot Water decrement (90ºC,1 hour)	2%max.
Length	6mm,12mm

 

Packing

200kgs net per parcel;12.8MT/1X20`FCL with pallet
 

Related Goods

               PP Fiber Twisted Bunchy 500T                                 PP Macro Fiber Embossed                                            Steel Fiber     
 

                PP Macro Fiber Wave Form                                Brass Coated Micro Steel Fiber                                  Glass Fiber              

Company Profile