Transparent Monofilament Sythetic Fiber for Uhpc for Municipal Road Bricks

• After-sales Service: None
• 10kgs Each Bag: D:0.2mm; L: 6/12mm
• Minimum Tensile Strength: >950MPa
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: Sythetic Fiber For UHPC
• Modulus: >12gpa
• Elongation at Break: ≤30%
• Density: 1.4G/Cm3
• Acid &Alkali Resistance: Excellent
• Moisture Content: ≤0.1%
• Appearance: Transparent Monofilament
• Transport Package: 10kgs Each Bag
• Specification: 100% UHPC
• Trademark: Briture
• Origin: China
• Production Capacity: 45000metric Ton/Year
• Package Size: 20.00cm * 15.00cm * 15.00cm
• Package Gross Weight: 10.100kg

Product Description

Product Description

UHPC special synthetic fiber uses hydrophilic modification technology for its surface treatment. It has excellent dispersibility in UHPC, and has good bonding performance with cement matrix materials, which can effectively reduce and inhibit UHPC plastic shrinkage, drying shrinkage, Micro-cracks caused by temperature changes and other factors significantly improve crack resistance, toughening , impact resistance, fire and explosion resistance of UHPC.

 

Application

1. Building decoration exterior wall     

2. UHPC carved artwork 

3. Cement Flower pot products

4. Municipal road bricks etc.

Specification

 

Fiber Dimension	D:0.2mm; L: 6/12mm
Minimum Tensile Strength	>950MPa
Modulus	>12GPa
Elongation at break	≤30%
Density	1.4g/cm3
Acid &Alkali Resistance	Excellent
Moisture Content	≤0.1%
Appearance	Transparent monofilament

Our Advantages

• No rusty 

• Excellent dispersity 

• Self compact

• Light and artistic 

• Colourfull
   

Useage

Dosage: the usual dosing amount is 5.0-50.0kg /m3( the corresponding volume dosing amount is 0.4-4.0%).

Length: The length of UHPC should be 6-12mm. According to different thickness of components. 

Stirring: After mixing the UHPC powder and water to make the slurry evenly, add the fibers, and then stir for 2 to 4 minutes, subject to the uniform dispersion of the fibers. 

Curing: The construction and curing process of UHPC after adding fiber is exactly the same as the system without fiber 

Packing

10kgs each bag, 5500kgs/1X20`FCL or 13000kgs/1X40`HQ without pallet.
 

Related Goods

               PP Fiber Twisted Bunchy 500T                                                 PP Macro Fiber Embossed                                            PP Macro Fiber Wave Form

                                  Steel Fiber                                                              Brass Coated Micro Steel Fiber                                             Glass Fiber

Company Profile