550MPa PP Fiber Hybrid Type for Industrial and Residential Floors

• Customization: Available
• Application: Concrete Reinforcement
• Color: White Mixed with Gray
• Model NO.: PP Fiber Hybrid Type
• Length: 38/48/54mm...
• Material: High-strength Polypropylene Fiber
• Tenacity: Medium Tenacity
• Type: Virgin Fiber
• Product Name: PP Fiber Hybrid Type
• Hybrid Ratio: 98% Twisted + 2% Mesh by Weight
• Additive Amount: 2.7-5.5kg/M3
• Break Strength: 550MPa Min.
• Transport Package: 1kg Per PE Bag, 10kg Per Plastic Woven Bag
• Specification: Twist with Mesh
• Trademark: None
• Origin: China
• HS Code: 5503400000
• Production Capacity: 3000metric Ton/Year
• Package Size: 30.00cm * 25.00cm * 15.00cm
• Package Gross Weight: 1.000kg

Product Description

550MPa PP Fiber Hybrid Type for Industrial and Residential Floors

Product Description

1. PP Fiber Twisted Bunchy is a 100% virgin blended copolymer synthetic structural macro-fiber successfully used as an alternative to steel fibers, welded wire mesh and conventional reinforcing bars in a wide variety of secondary reinforcement applications.
2. PP Fiber Hybrid type is actually a Hybrid of two fibers: A standard fibrillated mesh form Polypropylene Fiber to reduce and control shrinkage and temperature cracking. A twisted-bunchy form fiber made of strong synthetic copolymer, to increase the flexibility and breaking strength of concrete. It has high break strength, better dispersion and strong combining ability. It is widely used to instead of steel fibre to reinforce the cement concrete and crack-resistant.
 

Applying Instruction:

1. Ration design of the fibre concrete: Generally the recommended amount to add to the concrete is more than 2.7kg per sqm(0.3% by volume), reinforcement adding amount is 5.5kg, Compared with adding 47kg of steel fibre, 5.4kg polymer fibre has the same volume ratio to the concrete.
2. Length: 48mm to 54mm for common crack-resistant requirement.
3. Mixer Adoption: Double-axle horizontal compelling mixer is priority.
4. Mixing process: Crushed stones, fibers and sands are put into the mixer in succession. After stirring for two minutes, fiber will fully spread and then add cement and water and stir normally. The addition of materials also can be put into as common concrete, but the stirring time should be properly prolonged to make fiber to be completely mixed .
5. Shaping & Maintenance: There is no special requirement, may along the vibrating time for 30s, The maintenance of the fibre concrete should be done same as the normal concrete.
6. Application: Industrial and residential floors; Whitetoppings, bridge decks and pavements; Thin walled pre-cast (septic tanks, vaults, walls, etc.); Mass concrete
 

Specification

Index	Twisted Bunchy	Fibrillated Mesh
Raw Material	PP/PE polymer	PP
Appearance	Twisted Bunchy	Mesh form
Elastic Modulus	≥5000Mpa
Length	38/48/54mm...
Diameter	0.3mm (+/-0.05)	0.05mm (+/-0.005)
Melt Point	170ºC	160ºC
Density	0.91g/cm3
Break Strength	550Mpa min.
Acid&alkali resistance	Excellent

 

Packing

1. 1kg each PE bag, 10kgs each woven bag,16000kgs/1X40`HQ with pallet
2. 1kg each PE bag or water soluble paper bag, 11kgs each carton, 9900kgs/1X40`HQ with pallet.

 

Related Goods

               PP Fiber Twisted Bunchy Form                           PP Macro Fiber Embossed                                                       Steel Fiber 

                  Brass Coated Micro Steel Fiber                                      Glass Fiber                                                  Synthetic Fiber For UHPC

 

Certifications