Polypropylene PP Monofilament Fiber for Any Mortar Projects with Good Cracking Resistance

• Customization: Available
• Application: Concrete Reinforcement
• Color: White
• Model NO.: PP Fiber Monofilament
• Material: Polypropylene
• Tenacity: High Tenacity
• Type: Microfiber
• Raw Material: 100% Virgin Polypropylene
• Density(g/cm3): 0.91
• Tensile Strength (MPa): 500 Min.
• Elastic Modulus (MPa): 4500 Min.
• Transport Package: 1kg Per Bag, 30kgs Per Carton
• Specification: Polypropylene
• Trademark: Briture
• Origin: China
• HS Code: 5503400000
• Production Capacity: 1000kgs/Year
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg
• Lead Time: 15 days (1 - 10000 kg) ; To be negotiated ( > 10000 kg)

Product Description

 PP Fiber Monofilament

Product Description

Feature:
1.  Easy to be dispersed in mortar or concrete and no agglomeration, it can guarantee the property of crack resistance effectively.   
2. No need to change the proportion of mortar, just put the fibers into the mortar mixture and stir for a moment after adding water.
3. PP Fiber Monofilament with fine economic property: The equivalent diameter of the fiber is only φ 30um, so the ratio of diameter and surface area is high and on the basis of crack resistance, PP Fiber Monofilament can reduce the amount (to about 0.6kg/m 3 ).
4.  Easy to plaster: As the great number of thin fibers spread into mortar evenly, the plastering is much easily and this can improve the binding strength between surface and base.
5. PP Fiber Monofilament with stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.
Applying Instruction:
A). Compound Amount. To resist the common cracks on surfaces, 0.6kg/m3 fibers to cement paint is enough, and for reinforced application 0.9- 1kg/m3 is enough.
B). Stirring requirement. The proportion of cement, sand and aggregate is no need to be changed. Put cement,aggregate, additive and fiber together, then stir after adding enough water (Do not stir without water!) and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely.

Index	Standard	Index	Standard
Raw Material	100% virgin Polypropylene	Fiber Type	Monofilament (Microfiber)
Density(g/cm3)	0.91	Fiber Diameter (um)	30+/-5
Tensile Strength (Mpa)	500 min.	Elastic Modulus (Mpa)	4500 min.
Melting Point(ºC)	160- 170	Length (mm)	6, 12, 18...
Crack Elongation (%)	15-20	Acid &Alkali Resistance	Strong

 