Easy Dispersing and Blending PP Fiber Twisted Bunchy Form for Cement Reinforcement

• Customization: Available
• Application: Construction
• Bonding Strength: High Bonding Strength
• Model NO.: PP Fiber Twisted Bunchy Form
• Raw Material: PP/PE
• Elastic Modulus: 5000MPa
• Break Strength: Break Strength
• Appearance: Twisted Bunchy
• Transport Package: 1kg Each PE Bag, 10kgs Each Woven Bag,
• Specification: Polypropylene
• Trademark: Briture
• Origin: China
• HS Code: 5503400000
• Production Capacity: 1000kgs/Year
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 1.000kg
• Lead Time: 15 days (1 - 10000 Bags) ; 20 days (10001 - 20000 Bags) ; To be negotiated ( > 20000 Bags)

Product Description

 

PP Fiber Twisted Bunchy Form

Product Description

 

 

1. PP fiber Twisted Bunchy is used to instead of steel fiber for reinforcement to cement concrete. Compare          with steel fiber, it has the advantage of easy dispersing and blending, no damage to the mixing equipments, etc

2. The rigid polymer fibre is used polypropylene as its raw material, produced the rough surface treatment by special parallel thread extruding & twisting process. It has high break strength, better dispersion and strong combining ability, will be widely used to instead of steel fibre to reinforce the cement concrete and crack-resistant.
Applying Instruction
 Ration design of the fibre concrete:
Generally the recommended amount to add to the concrete is more than 2.7kg per sqm (volume ratio is 0.3%), reinforcement adding amount is 5.5kg, Compared with adding 47kg of steel fibre, 5.4kg polymer fibre has the same volume ratio to the concrete.
 Length: 54mm for common crack-resistant requirement.
 Mixing process:
 Crushed stones, fibers and sands are put into the mixer in succession. After stirring for two minutes, fiber     will fully spread and then add cement and water and stir normally.
 

  Shaping & Maintenance:
   There is no special requirement, may along the vibrating time for 30s, The maintenance of the fibre concrete should be done same as the normal
concrete.
Specification

Raw Material	PP/PE
Elastic Modulus	≥5000Mpa
Length	54mm (+/-5%)
Diameter	0.7mm (+/-5%)
Melt Point	170ºC
Density	0.91g/cm3
Break Strength	600Mpa
Break tensile ratio	15% min.
Appearance	Twisted Bunchy
acid&alkali resistance	Excellent

 