Twisted Bunchy Polypropylene PP Fiber for Concrete

• Customization: Available
• Application: Concrete Reinforcement
• Color: Grey
• Model NO.: Bunchy form
• Length: 54mm
• Material: High-strength Polypropylene Fiber
• Tenacity: High Tenacity
• Type: Microfiber
• MOQ: 1000kg
• Shelf Life: Two Years
• Raw Material: PP/PE
• Elastic Modulus: >=5000MPa
• Diameter: 0.7mm (+/-5%)
• Melt Point: 170
• Transport Package: 1kg Each PE Bag
• Specification: 5500kgs/1X20`FCL
• Trademark: Briture
• Origin: China
• HS Code: 5503400000
• Production Capacity: 10000mt/Year
• Package Size: 20.00cm * 20.00cm * 15.00cm
• Package Gross Weight: 20.000kg

Product Description

PP Fiber Twisted Bunchy Form

Product Description

1. This fibre is used to instead of steel fiber for reinforcement to cement concrete. Compared with steel fiber, it has the advantage of easy

dispersing and blending, no damage to the mixing equipments, etc

2. The rigid polymer fibre is used polypropylene as its raw material, produced the rough surface treatment by special parallel thread extruding &

twisting process. It has high break strength, better dispersion and strong combining ability, will be widely used to instead of steel fibre to reinforce the cement concrete and crack-resistant.

 

Guidelines for use

1. Ration design of the fibre concrete: Generally the recommended amount to add to the concrete is more than 2.7kg per sqm (volume ratio is 0.3%), reinforcement adding amount is 5.5kg, Compared with adding 47kg of steel fibre, 5.4kg polymer fibre has the same volume ratio to the concrete.

2. Length: 54mm for common crack-resistant requirement.

3. Matching Ratio: Usually, it is no need to Change the matching ratio of the concrete. Considering the requirement of fissure-resistant, the polymer fiber is recommend to combine with the PP fiber mesh form with the volume ratio of 1:1(0.9kg fiber-mesh to per sqm of cement concrete). .

4. Mixer Adoption: Double-axle horizontal compelling mixer is priority.

5. Mixing process: Crushed stones, fibers and sands are put into the mixer in succession. After stirring for two minutes, fiber will fully spread and then add cement and water and stir normally. The addition of materials also can be put into as common concrete, but the stirring time should be properly prolonged to make fiber com-pletely mixed
6. Shaping & Maintenance: There is no special requirement, may along the vibrating time for 30s, The maintenance of the fibre concrete should be done same as the normal concrete.

Specification

 

Raw Material	PP/PE
Elastic Modulus	≥5000Mpa
Length	54mm (+/-5%)
Diameter	0.7mm (+/-5%)
Melt Point	170ºC
Density	0.91g/cm3
Break Strength	600Mpa
Break tensile ratio	15% min
Appearance	Twisted Bunchy
acid&alkali resistance	Excellent

Packaging & Shipping

1kg each PE bag, 10kgs each woven bag, 5500kgs/1X20`FCL, 13000kgs/1X40`HQ without pallet.

Certifications