18mm 100% Virgin Polypropylene PP Monofilament Fiber for Concrete Construction

• Customization: Available
• Application Field: Machine Building, Industrial Building
• Colour: White
• Model NO.: PP Fiber Monofilament
• Fiber Type: 100% Virgin Polypropylene
• Luster: Bright
• Property: Acid and Alkali Resistance, Heat Resistance
• Strength: High Tenacity
• MOQ: 1000kgs
• Packing: 600/900/Kg Net Per PE Bag
• Application: Concrete Construction
• Other Name: Polypropylene Fiber
• Shelf Life: 2 Years
• Length: 12mm
• Transport Package: 600/900/Kg Net Per PE Bag
• Specification: 100% Virgin Polypropylene
• Trademark: Briture
• Origin: China
• HS Code: 391690900
• Production Capacity: 100000kgs/Year
• Package Size: 20.00cm * 20.00cm * 20.00cm
• Package Gross Weight: 25.000kg

Product Description

PP Fiber Monofilament

Product Description

Feature:

 

1. Easy to be dispersed in mortar or concrete and no agglomeration, it can guarantee the property of crack resistance effectively

2. No need to change the proportion of mortar, just put the fibers into the mortar mixture and stir for a moment after adding water.

3. It with fine economic property: The equivalent diameter of the fiber is only φ 30um, so the ratio of diameter and surface area is

high and on the basis of crack resistance, it can reduce the amount (to about 0.6kg/m 3 ).

4. Easy to plaster: As the great number of thin fibers spread into mortar evenly, the plastering is much easily and this can improve

the binding strength between surface and base.

5. It with stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.


Appling Instruction:

A). Compound Amount. To resist the common cracks on surfaces, 0.6kg/m3 fibers to cement paint is enough, and for reinforced application 0.9-1kg/m3 is enough.

B). Stirring requirement. The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water (Do not stir without water!) and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely.

Packaging & Shipping

600/900/1KG net per PE bag;18kgs net per plastic woven bag;12000kgs/1X20'FCL without pallet;25000kgs/1X40`HQ

Raw Material	100% virgin Polypropylene
Density(g/cm3)	0.91
Tensile Strength (Mpa)	500 min.
Melting Point(ºC)	160-170
Crack Elongation (%)	15-20