Wave Form Polypropylene PP Fiber for Easy Dispersion in Cement

• Customization: Available
• Application: Concrete Reinforcement
• Color: White
• Model NO.: wave form
• Material: Polypropylene
• Tenacity: High Tenacity
• Type: Virgin Fiber
• Fiber Type: Wave Form
• Fiber Dia.: 0.9+/-0.1mm
• Acid &Alkali Resistance: Strong
• Elastic Modulas (MPa): 5192
• Transport Package: 4kgs Each PE Bag
• Specification: 12960kgs/1X40`HQ
• Trademark: Briture
• Origin: China
• HS Code: 3902100090
• Production Capacity: 50 Mt/Year
• Package Size: 20.00cm * 20.00cm * 15.00cm
• Package Gross Weight: 20.000kg

Product Description

Polypropylene Fibre Wave Form

Properties

PP fibre Undee form can be instead of steel fiber in cement concrete for anti-crack. Easy to disperse and construct.

Usage

1. Suggestion of Additive rate: 5.4kg fibre in one cubic meter concrete. (not less than 2.7kg/M3)

2. Technic of mixture:Put the fibre into detritus first, then put grit to mix for about 2minutes, to make the fibre be dispersed. Then put cementand water to mix as per normal technic.

Benefits

Strength:
1.Reduces concrete cracking; Improve the tensile strength, flexural strength and fracture strength of concrete.
2.Reduce breakage in the event of an earthquake or other serious natural disaster.
3.Reduction of fatal defects inside concrete; Improve the impermeability of concrete.
4.Protects the rebar from corrosion; Improve the durability of concrete structures.
5.Improve the wear resistance of concrete.
6.No wear and tear on mixing equipment.
7.Prevent tire damage.

Application

1.It is used for culvert support, natural terrain revetment and other support projects, because it has high bending and tensile strength.
2.It is used for leakage prevention in reservoirs, low-pressure water pipes and basements due to its excellent crack resistance.
3.It is used in high-speed flow areas, such as spillways and rams in water conservancy and hydropower projects, because of its excellent impact and wear resistance.
4.It is suitable for concrete works under seawater corrosive conditions, as it is made of synthetic resin with the properties of steel fibers.
5.It is used in projects that bear live loads, such as highway bridges, railways, etc., because it has excellent properties such as high fracture toughness, tensile resistance, and fatigue resistance

Specification

Raw Material	Polypropylene
Fiber Type	wave form
Length	24-60mm
Fiber Dia.	0.9±0.1mm
Melting Point(ºC)	160-170
Acid &Alkali Resistance	Strong
Crack Elongation	15-20%
Elastic Modulas (MPa)	5192
Tensile Strength(MPa)	400 min.