High Quality Monofilament Polypropylene Fibre PP Fiber for Concrete

• Customization: Available
• Fiber Type: Filament
• Application: Concrete Reinforcement.
• Model NO.: monofilament
• Raw Material: Polypropylene
• Crack Elongation: 15-20%
• Fiber Dia: 0.03+/-0.005mm
• Melting Point(℃): 160—170
• Acid &Alkali Resistance: Strong
• Tensile Strength (MPa): 500MPa Min.
• Length: 6mm/12mm/19mm etc..
• Usage: Concrete
• Material: 100% Polypropylene
• Color: White
• Function: High Strength Fiber
• Width: None
• Transport Package: 1 Kgs Net Per PE Bag; 20 Kgs Net Per PE Bag
• Specification: monofilament
• Trademark: Briture
• Origin: China
• HS Code: 5503400000
• Production Capacity: 2000mts / Year
• Package Size: 110.00cm * 110.00cm * 180.00cm
• Package Gross Weight: 25.200kg

Product Description

High Quality Monofilament Polypropylene Fibre PP Fiber for Concrete

Product Description:

Polypropylene Fiber (PP Fiber) is made from 100% virgin PP granular, after extruding from different mould and technology, we can get 4 different types of fiber, including Monofilament form, Fibrillated Mesh form, Twisted Bunchy and Wave form with different size. These fiber can improve the reinforcement of mortar or concrete performance effectively to make them strong and protect the projects


 

Function:

1) Resist to shrink & crack
2) Increase seepage resistance
3) Increase friction resistance
4) Increase freezing & thawing resistance
5) Improve tendons protection
6) Replace steel net (using in plastering)
7) Prevent mortar split and crackle expansion
8) Increase impact resistance and peeling resistance

FEATURE:
1, Easy to be dispersed in mortar or concrete and no agglomeration, it can guarantee the property of crack resistance effectively
2. Easy to be used: No need to change the proportion of mortar, just put the fibers into the mortar mixture and stir for a moment after adding water.
3. It with fine economic property: The equivalent diameter of PP monofilament is only φ 0.03mm, so the ratio of diameter and surface area is high and on the basis of crack resistance, it can reduce the amount (to about 0.6kg/m 3 ).
4. Easy to plaster: As the great number of thin fibers spread into mortar evenly, the plastering is much easily and this can improve the binding strength between surface and base.
5. It with stable chemical property, strong acid &alkali resistance, and can be used in any engineering projects.

APPLYING INSTRUCTION:
A). Compound Amount. To resist the common cracks on surfaces, 0.6kg/m3 fibers to cement paint is enough, and for reinforced application 0.9-1kg/m3 is enough.
B). Stirring requirement. The proportion of cement, sand and aggregate is no need to be changed. Put cement, aggregate, additive and fiber together, then stir after adding enough water (Do not stir without water! ) and time for stirring can be prolonged for 2~3 minutes in order to make the compound mix completely.

Suitable Project

1. Be suitable for the water-proof layer, floor, inner & outer wall of industrial and civil construction.
2. Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
3. Increase cracking & seepage resistance of the ground in natatorium, swimming pool, pond and ditch.
4. Be suitable for any mortar projects and fine aggregate concrete projects

Packing:

Packing one:

1).: 600g, 900g, 1kg net per PE bag
2).: 18kgs/ 20kgs per plastic woven bag
3).: 9540kgs/1X20`FCL without pallet
4).: 22000kgs/1X40`HC without pallet




Packing two:

1).: 600g, 900g or 1kg net per water soluble paper bag.
2).: 20kgs/ 25kgs per carton
3).: 7200kgs/1X20`FCL without pallet
4).: 16740kgs/1X40`HC without pallet

 

Delivery: 
2-3weeks after all thing be confirmed.